Samples of Cor-Ten steels have been subjected to surface treatment, by coating Al and followed by nitridation. High-temperature corrosion tests were carried out using a Thermo Gravimetry Analysis / Magnetic Suspension Balance (TGA/MSB). The Nitridation process was performed at 550°C for 3, 5, 4, 7 and 20 hours under flowing N2 and NH3 gases. Corrosion tests were performed for 50 hours at 650°C. After the oxidation, sample were characterized using X-Ray Diffractometer (XRD) to determine the crystal structure, and then using Scanning Electron Microscope (SEM) to observe the microstructure and hardness of the alloys by aloowing Micro Hardness Tester. It can be concluded that sample nitridized for 5 hours showed the lowest corrosion rate or highest corrosion resistance, due to the corrosion barrier was Al2O3 protective layer. The hardness of Cor-Ten increased from 137 VHN to 340VHN (after nitridation), and to 744 VHN after Al deposition and nitridation for 5 hours. The increase of hardness might be associated with the formation of aluminum nitride.

Keywords: Al Deposition, Corrosion Resistant, Cor-Ten, Nitridation, TGA/MSB, XRD, SEM

Dani M., Wagiyo H., Teguh S.P.P., Susi I., J. Mikroskopi dan Mikroanalisis, Vol.6, No.1, 2003.

Lai G.Y., “High Temperature Corrosion of Engineering Alloys”, Group Leader High Temperature Alloys Haynes International, Inc. Kokomo, Indiana, 1990.

Robergo P. R., “Handbook of Corrosion Engineering”. Mc.Graw-Hill. New York, 2000.

Untoro P., Wagiyo H., Workshop on Corrosion using TGA/MSB, National Nuclear Energy Agency (BATAN), Serpong, 2002.

Wagiyo H., Sulistioso G.S., Siti M., Pengaruh Nitridisasi Terhadap Ketahanan Korosi Temperatur tinggi Bahan SS312A, Prosiding Pertemuan Ilmiah Iptek Bahan, 2004.

Wasa K. And Hayakawa S., Handbook of Sputter Deposition Technology, Principle, Technology and Applications, Noyes Publication, (1992)

Wright I.G., High-Temperature Corrosion, Metal Handbook, Vol.13, 9th-ed, 1990.

http://www.adq.it/eng/products/prodo3.htm, 2003

http://www.ankersmid.com/China/PhysicCharacterisation/Products/Rubotherm, 2006.